Impact of different annealing methods on MEX-printed polyetherketoneketone parts

Butt, Javaid and Mohaghegh, Vahaj (2025) Impact of different annealing methods on MEX-printed polyetherketoneketone parts. The International Journal of Advanced Manufacturing Technology, 137 (9-10). pp. 5059-5080. ISSN 0268-3768

Text Antero_Manuscript_JB.pdf - Accepted Version Restricted to Repository staff only until 2 April 2026. Download (2MB) | Request a copy

Abstract

Material extrusion is an established category of additive manufacturing, primarily using thermoplastic materials for product development. The continuous quest for improved material properties and superior surface finish has driven significant interest in the development and application of advanced post-processing techniques. In this work, Antero 800NA has been used, which is a Polyetherketoneketone thermoplastic of the polyaryletherketone family, with excellent mechanical and thermal properties as well as high chemical resistance. To enhance the performance of Antero 800NA parts, three annealing methods were used in this work. They include oven annealing, fluidised bed annealing, and metal plate annealing. Temperatures of 160 °C, 180 °C, and 200 °C were used for three different time intervals of 1, 2, and 3 h. Metal plate annealing showed overall better dimensional integrity and surface finish compared to oven and sand annealing. However, sand annealing showed reduced dimensional variations at the 2-h annealing time-interval for all three temperatures. Tensile testing showed varying results with sand annealing, oven annealing, and metal plate annealing showing higher tensile strength at 160 °C, 180 °C, and 200 °C, respectively. Microstructural analysis showed a compact and cohesive structure with finer microvoids for high tensile strength specimens and larger voids as well as delamination for low tensile strength Antero 800NA specimens. Metal plate annealing also demonstrated higher hardness values, whereas oven and sand annealing showed consistent but lower values compared to metal plate annealing. These results provide a comprehensive comparison of three distinct annealing methods for Antero 800NA parts that can offer valuable insights into optimising post-processing techniques for engineering applications requiring enhanced performance of additive manufactured Antero 800NA parts.

Item Type:	Article
Identification Number:	10.1007/s00170-025-15482-2
Dates:	Date Event 27 March 2025 Accepted 2 April 2025 Published Online
Uncontrolled Keywords:	additive manufacturing, material extrusion, fused deposition modelling, annealing, fused filament fabrication, Antero 800NA, PEEK, PAEK
Subjects:	CAH10 - engineering and technology > CAH10-01 - engineering > CAH10-01-02 - mechanical engineering
Divisions:	Faculty of Computing, Engineering and the Built Environment > College of Engineering
Depositing User:	Gemma Tonks
Date Deposited:	25 Apr 2025 14:14
Last Modified:	25 Apr 2025 14:14
URI:	https://www.open-access.bcu.ac.uk/id/eprint/16317

Actions (login required)

View Item